Material: Stainless Steel
Application: Metal Processing Machinery Parts
Products Range:
| Material | Typical Values | |||||||
| Designation Code | Density g/cm3 | Tensile Properties | Young's modulus, Gpa | Un-notched Charpy Impact Energy,J | Hardness,Rockwell | |||
| UTS. Mpa | Y.S. (0.2%), Mpa | Elongation (in 25.4mm) % | Macro (apparent) | Micro (converted) | ||||
| MIM-Fe2Ni | 7.8 | 280 | 115 | 25 | 55 HRB | 50HRC | ||
| MIM-Fe8Ni | 7.8 | 450 | 12 | 84HRB | 50HRC | |||
| MIM-2200 (as sintered) | 7.8 | 290 | 125 | 40.0 | 190 | 135 | 45 HRB | |
| MIM-2700 (as sintered) | 7.8 | 415 | 255 | 26.0 | 190 | 175 | 69 HRB | |
| MIM-4605 (as sintered) | 7.8 | 440 | 205 | 15.0 | 200 | 70 | 62 HRB | |
| MIM-4605 (Q&T) | 7.8 | 1655 | 1480 | 2.0 | 205 | 55 | 48 HRC | 55 HRC |
| MIM-304L | 7.8 | 500 | 70 | 60 HRB | ||||
| MIM-316L (as sintered) | 7.85 | 520 | 175 | 50.0 | 190 | 190 | 67 HRB | |
| MIM-410 | 7.7 | 900 | 7 | 40 HRC | ||||
| MIM-420 (heat treated) | 7.7 | 1380 | 1200 | 12 | 190 | 40 | 45-60HRC | |
| MIM-430L (as sintered) | 7.8 | 410 | 240 | 25.0 | 210 | 150 | 65 HRB | |
| MIM-440C | 7.8 | 700 | 590 | 15 | 45-60HRC | |||
| MIM-17-4PH (as sintered) | 7.8 | 900 | 730 | 6.0 | 190 | 140 | 27 HRC | |
| MIM-17-4PH (heat treated) | 7.8 | 1190 | 1090 | 6.0 | 190 | 140 | 33 HRC | 40 HRC |
| Material | Density( g/m 3) | Tensile Strength( Mpa) | elastic modulus(Gpa) | (thermal conductivity) W/(mk) | ( Thermal Expansion) 10-6/k |
| Copper(Cu) | 8.9 | 100 | 130 | 250 | 13 |
| Invar(fe-36ni) | 8 | 300 | 205 | 20 | 5 |
| Kovar or F15 (Fe-29ni-17co) | 8.0 | 480 | 200 | 17 | 4.9 |
| Molybdenum-copper (Mo-15cu) | 10 | 210 | 280 | 170 | 7 |
| Molybdenum-copper (Mo-20cu) | 9.9 | 200 | 280 | 145 | 6.5 |
| Tungsten-copper (W-10cu) | 17 | 500 | 340 | 209 | 6 |
| Tungsten-copper (W-20cu) | 16 | 560 | 290 | 247 | 7 |
| Tungsten-copper (W-30cu) | 14 | 420 | 260 | 260 | 11 |